Tilt implantation for forming finfets

ABSTRACT

One embodiment of the instant disclosure provides a method for fabrication of fin devices for an integrated circuit, which comprises: forming a plurality of semiconductor fin structures, the fin structures including sidewalls and tops exposed from conformal masking; performing channel implantation at a tilt angle to form a doped region along the sidewalls and the tops of the fin structures, the fin structures being maintained at an elevated temperature during the channel implantation to prevent amorphization thereof during channel implantation; and forming at least one field effect transistor from the fin structures, the field effect transistor having a threshold voltage that is based on the channel implantation.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional application of U.S. patent applicationSer. No. 14/029,848, entitled “TILT IMPLANTATION FOR FORMING FINFETS,”filed Sep. 18, 2013, which is incorporated herein by reference in itsentirety.

TECHNICAL FIELD

The technology described in this disclosure relates generally tosemiconductor fabrication and more particularly to methods forfabrication of fin devices for integrated circuits.

BACKGROUND

The semiconductor integrated circuit (IC) industry has experienced rapidgrowth. Technological advances in IC materials and design have producedgenerations of ICs where each generation has smaller and more complexcircuits than the previous generation. For example, the semiconductorindustry has sought to decrease the size of memory cells. One strategythat has been employed includes the use of multiple gate transistors,including fin field effect transistors (FinFETs).

SUMMARY

The present disclosure is directed to methods for fabrication of findevices for an integrated circuit. In an exemplary method forfabrication of fin devices for an integrated circuit, a plurality ofsemiconductor fin structures are formed, the fin structures includingsidewalls and tops exposed from conformal masking. A channelimplantation is performed at a tilt angle to form a doped region alongthe sidewalls and the tops of the fin structures, the fin structuresbeing maintained at an elevated temperature during the channelimplantation to prevent amorphization thereof during channelimplantation. At least one field effect transistor is formed from thefin structures, the field effect transistor having a threshold voltagethat is based on the channel implantation.

In another exemplary method for fabrication of fin devices for anintegrated circuit, a plurality of semiconductor fin structures areformed, the fin structures including sidewalls and tops exposed fromconformal masking. At a fin recess stage, a channel implantation processis performed at a tilt angle to form a doped region along the sidewallsand the top of each of the exposed fin structures, the semiconductormaterial being maintained at an elevated temperature of no less thanabout 400 degree Celsius during the channel implantation to preventamorphization of the fin structures during channel implantation. Atleast one field effect transistor is formed from the fin structures, thefield effect transistor having a threshold voltage that is based on thechannel implantation.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 depicts a cross-sectional view of an example intermediate stagein the fabrication of a fin field effect transistor (FinFET).

FIGS. 2A, 2B, 2C, 2D, 2E, and 2F depict cross-sectional views ofintermediate stages of an example fabrication process for forming findevices for an integrated circuit.

FIG. 3 depicts a flowchart illustrating aspects of an exampleimplantation approach for forming FinFET devices with multiple thresholdvoltages.

FIG. 4 depicts an example graph illustrating implantation dose versustilt angle, where the curves represent implantation dose at a topportion and a sidewall portion of a fin device.

FIGS. 5A, 5B, 5C, 5D, and 5E depict cross-sectional views ofintermediate stages of an example fabrication process for forming P-typeand N-type fin devices of different threshold voltages.

FIG. 6 is a flowchart illustrating an example method for fabrication offin devices for an integrated circuit.

DETAILED DESCRIPTION

The present disclosure provides fin field effect transistors (FinFETs),and processes for fabricating the same, where the FinFETs may havemultiple, tunable threshold voltages. Being able to control thethreshold voltage in a device may be used to provide power savings inthe device without commonly encountered performance degradation. Forexample, an electronic device having FETs with two different thresholdvoltages (e.g., V_(t2)<V_(t1)) may be operated effectively in both a lowpower mode when a supply voltage Vdd is V_(t2)<Vdd<V_(t1), and in a highpower mode when Vdd is greater than V_(t1). The use of multiple, tunablethreshold voltages may have numerous other uses in devices.

FIG. 1 depicts a cross-sectional view of an example intermediate stagein the fabrication of a FinFET. In the example intermediate stage, finstructures 102 may be formed in a semiconductor material 104. Thesemiconductor material 104 may be, for example, monocrystalline siliconof a particular conductivity type (e.g., N-type silicon or P-typesilicon). In the example of FIG. 1, the fin structures 102 may haveheights 106 of approximately 25 nanometers and widths 108 ofapproximately 10 nanometers, and adjacent fin structures 102 may beseparated by a spacing 110 of approximately 38 nanometers. Such heights106, widths 108, and spacings 110 are exemplary only, and numerous otherdimensions may be used in other examples. The fin structures 102 mayinclude sidewall portions and top portions (e.g., exemplary sidewallportions 120 and top portion 122, as depicted in FIG. 1).

In the example of FIG. 1, a dopant implantation (symbolized by an arrow112) may be performed at a tilt angle 116 to form a doped region alongthe sidewall portions and the top portions of the fin structures 102. Inparticular, the tilt angle 116 may be chosen to cause an amount ofdoping at the sidewall portions and the top portions of the finstructures 102 to be approximately equal. In some examples, the topportions may have a slightly higher amount of doping as compared to thesidewall portions, but the difference in doping between the top andsidewall portions may be substantially reduced by selecting anadequately large tilt angle 116. For example, a dopant implantationperformed at too low a tilt angle 116 may cause the top portions of thefin structures 102 to be more heavily doped as compared to parts of thesidewall portions (e.g., bottom parts of the sidewall portions that arenear the substrate 104). The tilt angle 116 may be greater than 45degrees (e.g., 56 degrees), where the tilt angle 116 may be measuredrelative to a plane 114 that is substantially parallel to sidewalls ofthe fin structures 102.

In other examples, the tilt angle 116 may be chosen to be a maximum tiltangle that is allowed by the fin structures 102, where the maximum tiltangle is the largest angle that allows a particular fin structure toreceive a dopant without the dopant being impeded by a fin structurethat is adjacent to the particular fin structure. Although the exampleof FIG. 1 depicts the single arrow 112 to illustrate an angle of thedopant implantation, it should be understood that all of the finstructures 102 may receive the dopant via the implantation process. Inother examples, certain of the fin structures 102 may be masked, suchthat doped regions are not formed in the masked fin structures. Themasking may be used, for example, to protect PMOS fin structures whileimplanting NMOS fin structures, and vice versa.

Following the dopant implantation, one or more field effect transistorsmay be formed using the fin structures 102. The one or more field effecttransistors formed may be FinFETs (e.g., multiple gate FinFETtransistors). The subsequent steps used in forming the one or more fieldeffect transistors may include, for example, formation of a gatestructure substantially over the fin structures 102. A typical FinFETmay be fabricated with the vertical fin structures 102 extending fromthe substrate 104, where the fin structures 102 may be formed by, forexample, etching away a portion of a silicon layer of the substrate 104.A channel portion of the FinFET may be formed in the vertical finstructures 102. The gate structure may be provided substantially overthe fin structures 102 (e.g., the gate structure may wrap the finstructures 102).

The field effect transistors formed from the fin structures 102 may eachbe characterized as having a threshold voltage. The threshold voltagemay be a value of the gate-source voltage when a conducting channel ofthe transistor just begins to connect source and drain contacts of thetransistor, allowing significant current to flow. In the example of FIG.1, the threshold voltage for the field effect transistors may bedependent on aspects of the dopant implantation. For example, the finstructures 102 may be comprised of a silicon material, and the dopantimplantation may use a dopant that includes germanium, such that thedoped region formed by the dopant implantation includes the germanium(e.g., the doped region may include silicon germanium (SiGe)). Thegermanium implantation may be used to change the threshold voltage ofthe field effect transistors.

In one example, a particular fin structure of the fin structures 102 maycause a field effect transistor to have a first threshold voltage if theparticular fin structure is not doped via the germanium dopantimplantation. However, if the particular fin structure is subject to thegermanium dopant implantation, the field effect transistor may insteadhave a second threshold voltage that is different from the firstthreshold voltage. In one example, the threshold voltage of the fieldeffect transistor may be changed by controlling a dosage of thegermanium dopant implantation, where a magnitude of the change in thethreshold voltage may be proportional to the dosage. In this manner, thethreshold voltage of the field effect transistor may be tuned bycontrolling aspects of the germanium dopant implantation.

The dopant implantation may be performed at an elevated temperature. Inone example, an atmosphere in which the dopant implantation occurs maybe heated to a temperature that is greater than approximately 450degrees Celsius, and the wafer itself (i.e., including the substrate 104and the fin structures 102) may be heated to a temperature that isgreater than approximately 400 degrees Celsius. The elevated temperaturefor the dopant implantation may substantially prevent amorphization(e.g., damage to) of the fin structures 102 during the dopantimplantation. Prevention of the amorphization of the fin structures 102may lower a number of defects in the fin structures 102.

FIGS. 2A, 2B, 2C, 2D, 2E, and 2F depict cross-sectional views ofintermediate stages of an example fabrication process for forming findevices for an integrated circuit. In FIG. 2A, a substrate 10 is shownhaving a cap layer or dielectric liner 18 formed thereon. The substrate10 may be formed of silicon, for example. Although the substrate 10 maybe depicted in FIG. 2A as a bulk wafer including a single material(e.g., a bulk silicon wafer), in other examples, asemiconductor-on-insulator or silicon-on-insulator (SOI) wafer mayinstead be used. Where such an SOI wafer is used, the dielectric liner18 may be formed substantially over a top silicon layer of the SOIwafer, where the SOI wafer may also include an insulating layer (e.g.,an oxide layer) that is formed between the top silicon layer and asilicon base layer (e.g., a bottom silicon layer).

Any suitable material for the substrate 10 may be used, and the materialfor the substrate 10 may not be limited to silicon. For example, thesubstrate 10 may be a bulk substrate that may include gallium arsenide,germanium, or any other material or combination of materials. Further,the substrate 10 may include other features or structures that areformed on or in the substrate 10 in previous processing steps. Thedielectric liner 18 may include a dielectric material that enablesetching of the substrate 10. In one example, the substrate 10 may bemonocrystalline silicon, and the dielectric liner 18 may include siliconnitride. Liner 18 may be deposited substantially over the substrate 10.

FIG. 2B depicts an example patterning of the dielectric liner 18. Thepatterning may be performed using, for example, a lithographicpatterning process. The patterning may include steps for formingsub-minimum feature-sized fins (e.g., steps that allow fins to havewidths that are less than or equal to a minimum feature size achievableby lithography, such as a spacer image transfer (SIT) process.

FIG. 2C depicts an example patterning of the substrate 10 to form fins20, 22, where features of the patterned dielectric liner 18 may be usedas a mask in the patterning of the substrate 10. For example, after thedielectric liner 18 is patterned, an etch process may be used to removea portion of the substrate 10, thus forming the fins 20, 22. The etchprocess may include, for example, a reactive ion etch (RIE) process. Asillustrated in FIG. 2C, the fins 20, 22 include sidewall portions andtop portions (e.g., sidewall and top portions similar to those depictedin FIGS. 1 at 120 and 122, respectively).

The substrate 10 may provide a semiconductor material from which finfield effect transistors (FinFETs) may be formed. For example, thesubstrate 10 may include a silicon material that has been doped to be ofan N-type conductivity or a P-type conductivity. In one example, the fin20 may be used for forming an nFET device, and the fin 22 may be usedfor forming a pFET device. In other examples, both of the fins 20, 22may be employed to form devices of a single type (i.e., the fins 20, 22may both be used in forming nFETs, or the fins 20, 22 may both be usedin forming pFETs).

FIG. 2D depicts a first example dopant implantation (symbolized byarrows 24) that is performed at a tilt angle. The first dopantimplantation may form a doped region along sidewalls and tops of thefins 20, 22, where the doped region may include a dopant used in thefirst dopant implantation. The first dopant implantation may beperformed at a fin recess stage of the transistor fabrication process,such that the first dopant implantation may be performed prior toforming gate structures on the substrate 10. Performing the first dopantimplantation at this stage in the fabrication process may allow a largertilt angle to be used, where the tilt angle may be measured from a planethat is substantially parallel to the sidewalls of the fins 20, 22. Forexample, if the first dopant implantation is performed after theformation of the gate structures on the substrate 10, the tilt angle maybe constrained to a maximum of approximately 19 degrees. The tilt anglemay be constrained to the maximum of approximately 19 degrees due to theheight of the gate structures. For example, the height of the gatestructures may be greater than the height of the fins 20, 22, such thatone or more of the fins 20, 22 cannot receive a dopant unless the tiltangle of the first dopant implantation is constrained to an angle ofapproximately 19 degrees or lower. This constraining of the tilt anglemay be known as the shadowing effect. The constraining of the tilt anglemay be disadvantageous, as implanting a dopant on the sidewalls of thefins 20, 22 may be difficult due to the relatively low tilt angle.

By contrast, if the first dopant implantation is performed prior toforming the gate structures, as illustrated in FIG. 2D, the larger tiltangle may be used (e.g., the tilt angle 116 as illustrated in FIG. 1,which may be greater than 45 degrees or set to a maximum tilt angle asallowed by adjacent fin structures). The use of the larger tilt anglemay allow an amount of doping at the tops and the sidewalls of the fins20, 22 to be substantially equal. Further, performing the first dopantimplantation at the larger tilt angle may cause an amount of doping atuppermost portions of the sidewalls and bottom portions of the sidewallsto be substantially equal. Achieving equal doping throughout the topsand sidewalls of the fins 20, 22 may be known as conformal doping. Theapproximately equal doping throughout the tops and sidewalls of the fins20, 22 may be evidenced by the thickness of the doped region in the fins20, 22. As described above, the first dopant implantation may cause thedoped region to be formed along the sidewalls and the tops of the fins20, 22. In the conformal doping implantation at the larger tilt angle,the thickness of the doped region may be approximately equal in the topand sidewall portions of the fins 20, 22.

A dopant used for the first dopant implantation 24 may includegermanium. In one example, where the fins 20, 22 are formed in a siliconmaterial, the germanium dopant may form a dipole with the siliconmaterial. The dipole formation may be used to tune a threshold voltageof a FinFET transistor that is formed using the fins 20, 22. In oneexample, the threshold voltage the FinFET transistor may be changed bycontrolling a dosage of the germanium dopant implantation, where amagnitude of the change in the threshold voltage may be proportional tothe dosage. For example, when the field effect transistor is a p-typefield effect transistor, the germanium dopant implantation may reducethe threshold voltage of the field effect transistor, such that a higherdosage causes a greater reduction of the threshold voltage. Conversely,when the field effect transistor is an n-type field effect transistor,the germanium dopant implantation may increase the threshold voltage ofthe field effect transistor, such that a higher dosage causes a greaterincrease in the threshold voltage.

Although both of the fins 20, 22 may receive the dopant in the exampleof FIG. 2D, in other examples, one or more of the fins 20, 22 may bemasked during the first dopant implantation. By masking the one or moreof the fins 20, 22, certain of the fins 20, 22 may undergo the thresholdvoltage tuning caused by the first dopant implantation, while other finsmay be unaffected.

The first dopant implantation may be performed at an elevatedtemperature (e.g., greater than 400 degrees Celsius) to preventamorphization of the fins 20, 22 during the dopant implantation. Forexample, an atmosphere in which the first dopant implantation occurs maybe heated to a temperature of greater than approximately 450 degreesCelsius, and the wafer itself (e.g., including the substrate 10 and thefins 20, 22 formed on the substrate 10) may be heated to a temperatureof greater than approximately 400 degrees Celsius during the dopantimplantation. Amorphization of the fins 20, 22 may occur at atmospheretemperatures that are less than 450 degrees Celsius, where theamorphization may be evidenced by necking in the fins 20, 22 or lateralamorphization merging at the center of the fins 20, 22 (e.g., in a finhaving a nominal width of 10 nanometers, the necking or the lateralamorphization may cause the fin to have a fin width that is less thanthe nominal fin width of 10 nanometers). In one example, a heater (e.g.,a beam line heater manufactured by Thermion Systems International, Inc.)may be used to heat the atmosphere and the wafer during the dopantimplantation.

FIG. 2E depicts a second tilt implantation (symbolized by arrows 26).The second tilt implantation may be performed in a tilt direction thatis opposite that of the first tilt implantation described above withreference to FIG. 2D. For example, the first tilt implantation may beconsidered to use a tilt in the −X direction, and the second tiltimplantation depicted in FIG. 2E may be considered to use a tilt in the+X direction. Thus, the process described in FIGS. 2D and 2E mayimplement a two-step implantation procedure, where the two steps may beused to ensure that all sides of the fins 20, 22 receive anapproximately equal dosage.

The second tilt implantation may be performed in a manner that issimilar to that used in the first tilt implantation, such that thesecond tilt implantation is performed i) at a tilt angle to achieveconformal doping along the sidewalls and tops of the fins 20, 22; ii) ata fin recess stage of the fabrication process (e.g., prior to forminggate structures on the substrate 10); and iii) at an elevatedtemperature (e.g., greater than approximately 400-450 degrees Celsius),where the elevated temperature prevents amorphization of the fins 20, 22during the dopant implantation. Further, the first and the second tiltimplantations may each use one half of a total dosage. For example, if atotal dosage to be delivered is 2×10¹⁵/cm², then the first implantationmay be used to deliver a germanium dosage of 1×10¹⁵/cm², and the secondimplantation may be used to deliver a germanium dosage of 1×10¹⁵/cm². Inthis manner, the different sides of the fins 20, 22 may each receivehalf of the total dosage.

FIG. 2F depicts a fin 27 following the first and the second tiltimplantations. The fin 27 may be, for example, either of the fins 20, 22as depicted in FIGS. 2C, 2D, and 2E. By performing both of the first andthe second tilt implantations at the larger tilt angle, a conformity ofthe resulting doping regions may be improved. As depicted in FIG. 2F,the sidewall portions of the fin 27 have doped regions of a thickness28, and the top portions of the fin 27 have doped regions of a thickness30. The thicknesses 28 and 30 may be approximately equal. Further, thethickness 28 of the doped regions of the sidewalls may be approximatelyequal at uppermost portions of the sidewalls and at bottom portions ofthe sidewalls.

FIG. 3 depicts a flowchart 300 illustrating aspects of an exampleimplantation approach for forming FinFET devices with multiple thresholdvoltages. At 302, well loop implant and well loop anneal steps may beperformed. The well loop implant step may be performed to define a largeregion of a semiconductor substrate as being N-type or P-type. Forexample, using the well loop implant step, a large region in a bulkN-type silicon substrate may be doped to be P-type silicon. Conversely,the well loop implant step may also be used to dope a large region in abulk P-type silicon substrate to be N-type silicon. The well loopimplant step may be performed, for example, when PMOS FinFETs are to beformed from an N-type silicon substrate or when NMOS FinFETs are to beformed from a P-type silicon substrate. The well loop anneal step may beperformed following the well loop implant step and may be used to reducean amount of defects caused by the well loop implantation process.

At 304, fin structures may be formed in the semiconductor material ofthe substrate (e.g., as described above, with reference to FIGS. 2A, 2B,and 2C). For example, the formation of the fin structures may includeforming a mask for etching the semiconductor material and performing asubsequent etch of the semiconductor material. At 306, a mask layer maybe deposited, where the deposited mask layer may be patterned using aresist layer and lithographic processing. The mask layer may be etchedaway from areas that will be implanted with a dopant (e.g., germanium)and maintained in areas that are to remain protected from the dopant. Ifa CMOS device is being formed with both nFET and pFET devices, then finstructures for the nFETs may be masked off during the pFET processing,and conversely, fin structures for the pFETs may be masked off duringthe nFET processing. At 308, an atmosphere in which the dopantimplantation will occur may be heated. For example, the atmosphere maybe heated to a temperature that is greater than 450 degrees Celsius.

At 310, a germanium dopant implantation is performed in the heatedatmosphere to form a doped region in the unmasked fin structures. Asillustrated in FIG. 3, the germanium dopant implantation may beperformed at a fin recess stage of the fabrication process, such thatthe implantation may be performed prior to forming gate structures onthe substrate. An energy of the germanium dopant implantation may beselected to be within a range of 1-4 KeV. The energy selected maydetermine whether the doping is conformal or uniform. The conformaldoping may cause the doped region to exist only around outer edges ofthe fin structures. For example, the fin structure 27 depicted in FIG.2F may have been doped in a conformal manner, such that the dopedregions exist only at the edges of the fin structure 27 and not withinan interior region of the fin structure 27. By contrast, the uniformdoping may cause the doped region to exist throughout an entirety of thefin structures (i.e., in the uniform doping, the germanium dopant may bepresent at the interior region of the fin structures and not only at theouter edges of the fin structures). An energy within a range ofapproximately 1-2 KeV may create a conformal germanium doped region, andan energy that is greater than approximately 4 KeV may create a uniformgermanium doped region.

The dosage of the germanium dopant implantation may be within a range ofapproximately 1×10¹⁵/cm² to 5×10¹⁵/cm². As described above, the totaldosage may be divided between first and second implantations performedat different tilt directions (e.g., a −X tilt direction and a +X tiltdirection, where one half of the total dosage is delivered at each ofthe two tilt directions). In one example, a threshold voltage of a fieldeffect transistor formed using the fin structures may be changed bycontrolling the dosage of the germanium dopant implantation, where amagnitude of the change in the threshold voltage may be proportional tothe dosage. In one example, a threshold voltage of a PMOS FET may bereduced by approximately 40 mV per 1×10¹⁵/cm² germanium dosage (e.g.,such that the threshold voltage may be reduced by 80 mV when doublingthe germanium dosage to 2×10¹⁵/cm², and so on). In another example, athreshold voltage of a NMOS FET may be increased by approximately 40 mVper 1×10¹⁵/cm² germanium dosage (e.g., such that the threshold voltagemay be increased by 80 mV when doubling the germanium dosage to2×10¹⁵/cm², and so on). In other examples, the change in the thresholdvoltage may not be proportional to the dosage (e.g., various othernon-linear relationships between threshold voltage and dosage may beused).

A temperature maintained throughout the germanium dopant implantationmay be within a range of 400-450 degrees Celsius, or the temperature maybe higher than this range. The germanium dopant implantation may beperformed at a tilt angle, as described above with respect to FIGS. 1,2D, and 2E. The tilt angle may be within a range of approximately 25-45degrees, for example. A twist angle of 0 degrees may be used in thegermanium dopant implantation.

At 312, a field effect transistor or transistors may be fabricated fromthe fin structures. The fabrication of the field effect transistor ortransistors may include forming a high dielectric constant gatedielectric and a gate conductor substantially over the fin structures.Other process steps may be performed in fabricating the field effecttransistor or transistors (e.g., oxide formation substantially over thefin structures, annealing steps, or deposition of a polysilicon layersubstantially over the fin structures, among others).

FIG. 4 depicts an example graph 400 illustrating implantation doseversus tilt angle, where the curves 402, 404 represent implantation doseat a top portion and a sidewall portion, respectively, of a finstructure. In FIG. 4, an x-axis may represent the tilt angle, where thetilt angle is measured from a plane that is substantially parallel tothe sidewall portion of the fin structure, and a y-axis may representthe implantation dose, where the dose is normalized to be within a rangeof 0.0 to 1.0. The graph 400 may thus illustrate a dose deviationbetween the top portion and the sidewall portion of the fin structure asa function of the tilt angle. As depicted in the graph 400, at lowertilt angles, the dose at the top portion of the fin 402 may besignificantly greater than the dose at the sidewall portion of the fin404. As the tilt angle increases, the dose at the sidewall portion ofthe fin 404 may increase, and the dose at the top portion of the fin 402may decrease. At a tilt angle of approximately 45 degrees, the dose atthe top portion of the fin 402 may be approximately equal to the dose atthe sidewall portion of the fin 404. The doses at the top and sidewallportions may be also be approximately equal at angles that are greaterthan 45 degrees.

FIGS. 5A, 5B, 5C, 5D, and 5E depict cross-sectional views ofintermediate stages of an example fabrication process for forming N-typeand P-type fin devices 20, 22 of different threshold voltages. In FIG.5A, fins 20 and 22 are depicted, where the fin 20 may be used to formone or more NFET devices, and where the fin 22 may be used to form oneor more PFET devices. The fins 20 and 22 may be formed in asemiconductor material of the substrate 10 (e.g., as described above,with reference to FIGS. 2A, 2B, and 2C). In FIG. 5B, a mask layer 23 maybe conformally formed substantially over the fin 20, and the fin 22 maycontinue to be unmasked. A first germanium dopant implantation process(symbolized by arrows 24) may be used to form doped regions within theunmasked fin 22. The fin 20 that is masked by the mask layer 23 may beprotected from the first germanium dopant implantation. In this manner,the NFET regions may be protected during processing of the PFET regions.FIG. 5C depicts the fin 22 as including a doped region 25 along sidewallportions and a top portion of the fin 22, where the doped region 25 maybe the result of the first germanium dopant implantation. In FIG. 5C,the mask layer 23 is removed from the fin 20.

In FIG. 5D, a mask layer 27 may be conformally formed substantially overthe fin 22, and the fin 20 may continue to be unmasked. A secondgermanium dopant implantation process (symbolized by arrows 26) may beused to form doped regions within the fin 20. In the example of FIGS. 5Band 5D, a direction of the tilt implantations as depicted by the arrows24, 26 is arbitrary (e.g., tilt implantations may be performed in both−X and +X tilt directions, despite the fact that only a single tiltdirection is depicted in each of the FIGS. 5B and 5D). The fin 22 thatis masked by the mask layer 27 may be protected from the secondgermanium dopant implantation. Thus, the PFET regions may be protectedduring processing of the NFET regions. FIG. 5E depicts the fin 20 asincluding a doped region 29 along sidewall portions and a top portion ofthe fin 20, where the doped region 29 may be formed as a result of thesecond germanium dopant implantation.

The selective masking of either of the NFET or PFET regions during thedopant implantation may be performed such that a threshold voltage ofthe NFET devices may be altered while not affecting the PFET devices,and vice versa. As described above, in examples where the fin structuresare formed in a silicon material and a dopant for the dopantimplantation is comprised of germanium, performing the germanium dopantimplantation may increase the threshold voltage in NFET devices anddecrease the threshold voltage in PFET devices. Thus, in order toincrease the threshold voltage in the NFET devices without causing acorresponding decrease in the threshold voltage in the PFET devices, andvice versa, the NFET and PFET regions may be selectively masked asdescribed in FIGS. 5A-5E. Further, by masking certain of the fins,multiple threshold voltages for FET devices may be achieved on a singlechip.

FIG. 6 is a flowchart 600 illustrating an example method for fabricationof fin devices for an integrated circuit. At 602, fin structures may beformed in a semiconductor material, where the fin structures may includesidewalls and tops. At 604, a dopant implantation may be performed at atilt angle to form a doped region along the sidewalls and the tops ofthe fin structures. The semiconductor material may be maintained at anelevated temperature during the dopant implantation, where the elevatedtemperature may substantially prevent amorphization of the finstructures during the dopant implantation. At 606, a field effecttransistor may be formed from the fin structures, where the field effecttransistor may have a threshold voltage that is based on the dopantimplantation.

Accordingly, one aspect of the instant disclosure provides a method forfabrication of fin devices for an integrated circuit, which comprises:forming a plurality of semiconductor fin structures, the fin structuresincluding sidewalls and tops exposed from conformal masking; performingchannel implantation at a tilt angle to form a doped region along thesidewalls and the tops of the fin structures, the fin structures beingmaintained at an elevated temperature during the channel implantation toprevent amorphization thereof during channel implantation; and formingat least one field effect transistor from the fin structures, the fieldeffect transistor having a threshold voltage that is based on thechannel implantation.

Accordingly, another aspect of the instant disclosure provides a methodfor fabrication of fin devices for an integrated circuit, whichcomprises: forming a plurality of semiconductor fin structures, the finstructures including sidewalls and tops exposed from conformal masking;at a fin recess stage, performing channel implantation at a tilt angleto form a doped region along the sidewalls and the top of each of theexposed fin structures, the semiconductor material being maintained atan elevated temperature of no less than about 400 degree Celsius duringthe channel implantation to prevent amorphization of the fin structuresduring channel implantation; and forming at least one field effecttransistor from the fin structures, the field effect transistor having athreshold voltage that is based on the channel implantation.

This written description uses examples to disclose the disclosure,including the best mode, and also to enable a person skilled in the artto make and use the disclosure. The patentable scope of the disclosuremay include other examples. It should be understood that as used in thedescription herein and throughout the claims that follow, the meaning of“a,” “an,” and “the” includes plural reference unless the contextclearly dictates otherwise. Also, as used in the description herein andthroughout the claims that follow, the meaning of “in” includes “in” and“on” unless the context clearly dictates otherwise. Further, as used inthe description herein and throughout the claims that follow, themeaning of “each” does not require “each and every” unless the contextclearly dictates otherwise. Finally, as used in the description hereinand throughout the claims that follow, the meanings of “and” and “or”include both the conjunctive and disjunctive and may be usedinterchangeably unless the context expressly dictates otherwise; thephrase “exclusive of” may be used to indicate situations where only thedisjunctive meaning may apply.

It is claimed:
 1. A method for fabrication of fin devices for anintegrated circuit, comprising: forming a plurality of semiconductor finstructures, the fin structures including sidewalls and tops exposed fromconformal masking; performing channel implantation at a tilt angle toform a doped region along the sidewalls and the tops of the finstructures, the fin structures being maintained at an elevatedtemperature during the channel implantation to substantially preventamorphization thereof during channel implantation; and forming at leastone field effect transistor from the fin structures, the field effecttransistor having a threshold voltage that is based on the channelimplantation.
 2. The method of claim 1, wherein performing channelimplantation comprises using a dopant that includes germanium, whereinthe doped region includes germanium, and wherein the semiconductor finstructure includes silicon.
 3. The method of claim 2, further comprisingheating the fin structure to an elevated temperature of no less thanabout 400 degree Celsius during channel implantation.
 4. The method ofclaim 3, further comprising forming a substantially conformal dopantprofile in the fin structure by performing implantation at energy levelfrom about 1 KeV to about 2 keV.
 5. The method of claim 3, furthercomprising forming a substantially uniform dopant profile in the finstructure by performing implantation at energy level greater than about4 KeV.
 6. The method of claim 1, further comprising: changing thethreshold voltage of the field effect transistor by controlling a dosageof the channel implantation, wherein a magnitude of the change in thethreshold voltage is proportional to the dosage.
 7. The method of claim1, further comprising: heating an atmosphere in which the channelimplantation is performed, wherein a temperature of the atmosphereduring the channel implantation is greater than about 450 degreesCelsius; and heating the fin structures during the dopant implantationto the elevated temperature, wherein the elevated temperature no lessthan approximately 400 degrees Celsius.
 8. The method of claim 1,wherein performing channel implantation at a tilt angle comprisesimplanting at a maximum tilt angle allowed by the fin structures,wherein the maximum tilt angle causes a particular fin structure toreceive a dopant without the dopant being impeded by a fin structurethat is adjacent to the particular fin structure, wherein the tilt angleis measured from a plane that is substantially parallel to a sidewall ofthe particular fin structure.
 9. The method of claim 1, whereinperforming channel implantation at a tilt angle comprises implanting attilt angle in a range of about 25 to about 45 degrees, wherein the tiltangle is measured from a plane that is substantially parallel to asidewall of a fin structure.
 10. The method of claim 1, whereinperforming channel implantation at a tilt angle comprises implanting attilt angle greater than about 45 degrees, wherein the tilt angle ismeasured from a plane that is substantially parallel to a sidewall of afin structure.
 11. The method of claim 1, wherein forming field effecttransistor from the fin structures comprises forming an n-type fieldeffect transistor, wherein performing the channel implantation increasesthe threshold voltage thereof.
 12. The method of claim 1, whereinforming field effect transistor from the fin structures comprisesforming a p-type field effect transistor, wherein performing channelimplantation decreases the threshold voltage thereof.
 13. The method ofclaim 1, wherein performing channel implantation at a tilt anglecomprises implanting at a tilt angle to cause an amount of doping at thetops and the sidewalls of the fin structures to be approximately equal.14. The method of claim 1, wherein performing channel implantation at atilt angle comprises implanting at a tilt angle to cause an amount ofdoping at uppermost portions of the sidewalls and bottom portions of thesidewalls to be approximately equal.
 15. The method of claim 1, whereinforming a plurality of semiconductor fin structures comprises formingthe fin structures on a substrate; and wherein performing channelimplantation at a tilt angle comprises performing channel implantationprior to forming gate structures on the substrate.
 16. The method ofclaim 15, wherein the channel implantation is performed at a fin recessstage.
 17. The method of claim 1, wherein the conformal maskingsubstantially prevents doped regions from being formed in the maskedregions.
 18. The method of claim 17, wherein the conformal masking isarranged to allow performing channel implantation at a tilt angle ofmore than about 45 degrees.
 19. A method for fabrication of fin devicesfor an integrated circuit, comprising: forming a plurality ofsemiconductor fin structures, the fin structures including sidewalls andtops exposed from conformal masking; performing channel implantation ata tilt angle to form a doped region along the sidewalls and the tops ofthe fin structures at an energy level in a range of about 1 KeV to about4 KeV, and wherein the fin structures is maintained at an elevatedtemperature during the channel implantation to substantially preventamorphization thereof during channel implantation; and forming at leastone field effect transistor from the fin structures, the field effecttransistor having a threshold voltage that is based on the channelimplantation.
 20. A method for fabrication of fin devices for anintegrated circuit, comprising: forming a plurality of semiconductor finstructures, the fin structures including sidewalls and tops exposed fromconformal masking; at a fin recess stage, performing channelimplantation at a tilt angle to form a doped region along the sidewallsand the top of each of the exposed fin structures, the semiconductormaterial being maintained at an elevated temperature of no less thanabout 400 degree Celsius during the channel implantation tosubstantially prevent amorphization of the fin structures during channelimplantation; and forming at least one field effect transistor from thefin structures, the field effect transistor having a threshold voltagethat is based on the channel implantation.